416S21不锈钢

圆钢--Φ10、20、30、40、50、60、70、80、90、100、200、300、400、500.

钢丝--Φ0.01、0.05、0.1-3.0-4.0-6.0

盘圆--Φ1-2-3-4-5-6-7-8-9-10。

板材--T:0.01-50mm*10*2000*L

铂族金属基难熔超合金 (Refractory Superalloys)Platinum Group Metals (Ir, Rh, Pt, Pd, Os and Ru) are promissing materials for base metals of refractory superalloys because of their high melting temperatures and superior oxidation resistance. Ir, Rh, Pt and Pd he the fcc structure similer to Ni, although Os and Ru he the hcp structure. Ir and Rh (fcc) can be equilibrated with the L12 structure (see Phase diagrams). Thus we are investigating Ir- or Rh-based refractory superalloys. Temprature dependence of the 0.2% flow stress during compression testing in as- cast Ir-base and Rh-base alloys with 15at% second elements, Ni-base, and W- base alloysMicrostructure of Ir-base alloys

416S21典型应用为：
●硫酸酸洗工厂用的加热管、容器、筐及链等。
●海水冷却热交换器、海洋产品管道系统、酸性气体环境管道。
●磷酸生产中的热交换器、蒸发器、洗涤、浸渍管等。
●石油精炼中的空气热交换器
●食品工程
●化工流程
●压氧气应用的阻燃合金

416S21合金特性编辑
●好的耐应力腐蚀开裂性能
●好的耐点腐蚀和缝隙腐蚀性能
●很好的抗氧化性和非氧化性热酸性能
●在室温和高达550℃的高温时都具有很好的机械性能
●具有制造温度达450℃的压力容器的认证

416S21合金应用领域编辑：416S21广泛应用于各种使用温度不超过550℃的工业领域。
416S21焊接编辑：416S21适合采用任何传统焊接工艺与同种材料或其金属焊接，如钨电极惰性气体保护焊、等离子弧焊、手工亚弧焊、金属极惰性气体保护焊、熔化极惰性气体保护焊，其中脉冲电弧焊是方案。在采用手工电弧焊时，推荐使用(Ar+He+H2+CO2)多种成份混合的保护气体。416S21的焊接必须在退火态进行，并使用不锈钢丝刷清理干净污渍、粉尘和各种记号。在焊缝根部焊接时，为得到的根部焊缝质量，操作必须非常小心(99.99)，这样在根部焊接完后焊缝就不产生氧化物。焊接热影响区产生的颜色要在焊缝区域未冷却时用不锈钢刷刷去。
变形高温合金按型质分为，即：1—表示固溶强化型铁基合金；2—表示时效硬化型铁基合金；3—表示固溶强化型镍基合金；4—表示时效硬化型镍基合金；5—表示固溶强化型钴基合金；6—表示时效硬化型钴基合金。 第二、三、四位数字表示合金的编号。
铸造高温合金编号为K+三位数字，如K403。位数字表示分类号，即：2—表示时效硬化型铁基合金；4—表示时效硬化型镍基合金；6—表示时效硬化型钴基合金。第二、三位数字表示合金的编号。焊接高温合金丝的编号为HGH+四位数字，含义与变形高温合金相同。
416S21是什么家的标准，材质证明。镍与钼和铜一起，对化学还原也有显著的抗性